Corrosion of Composite Uranium Nitride Fuels

Thomas Braine, Brian J. Jaques, Jennifer Watkins, Darryl P. Butt

Research output: Contribution to conferencePresentation

Abstract

Uranium mononitride (UN) has been identified as a possible accident tolerant fuel in nuclear reactors based on its high uranium density, thermal conductivity and low fission-gas release. Pure UN samples have been shown in studies to react with water at the operating temperatures of light water reactors, which make up the majority of reactors in the United States. Composite UN-UO 2 fuels might be optimized for corrosion resistance in these conditions. An autoclave was re-engineered for work with radioactive materials by creating safeguards to prevent radioactive material release. UN was prepared from elemental uranium using a hydride-dehydride-nitride thermal synthesis prior to mixing with up to 10 wt% UO 2 . UN-UO 2 composites were tested by placing samples in the water-filled autoclave at 320°C and 9 MPa. Pellets were characterized for weight change, surface hydration, and grain boundary deterioration using a sensitive digital balance, optical microscopy and electron microscopy. Corrosion products were identified using energy dispersive X-ray spectroscopy and X-ray diffraction. The amount of leached uranium in solution was measured using inductive coupled plasma mass spectroscopy.

Original languageAmerican English
StatePublished - 12 Jul 2015

EGS Disciplines

  • Ceramic Materials
  • Nuclear Engineering

Fingerprint

Dive into the research topics of 'Corrosion of Composite Uranium Nitride Fuels'. Together they form a unique fingerprint.

Cite this